Color:Black
Fe2O3:0.3%
Shape:Brick
Apparent Porosity:7-8%
Shape:Brick
Thermal Shock Resistance:Good
Fe2O3:0.3%
High temperature crushing strength:>35MPA
Cold crushing strength:>90MPA
Surface:Smooth And Flat
Thermal Shock Resistance:Good
Shape:Brick
Thermal Shock Resistance Temperature Range:Wide
Thermal Shock Resistance Durability:High
Material:High-grade Refractory Material
Loading softing temperature:>1750(T2)2KG/CM3
Thermal expansion Coefficient:4.2-4.8 (*10-6/℃)
Fe2O3:0.3%
High temperature crushing strength:>35MPA
Material:High-grade Refractory Material
Density:2.75g/cm3
Thermal Shock Resistance:High
Thermal Expansion Coefficient:Low
Color:White, Black, Gray, Etc.
Place of Origin::JIANGSU ,CHINA
name:Refractory Corundum mullite setter plate
Material::SIC
Type:Corundum Mullite Setter Plate
Color:White
Dimension:680*375*35mm
Material:99% alumina
Color:Ivory white
Dimension:ceramic sagger refractory
name:Refractory Plate Kiln Shelves
application:Industrial Kiln Furniture
using temperature:<1600℃