Product Details:
|
| Name: | Ceramic Diaphragm | Material: | 99% Alumina Ceramic |
|---|---|---|---|
| Color: | White | Size: | 500*400*80mm |
| Shape: | Box | Type: | Ceramic Box |
| Acid Fastness: | 99% | Grain Size: | 0.5~2um |
Alumina Ceramic Diaphragm in Chrome Electroplating
1. Description
Alumina Ceramic diaphragm is Used in decorative chromium and hard chromiumplating to lift impurities. In the production of decorative chromium and hard chromium, due to workpiece cleaning dirtyreasons, making bath cationic impurities in gradually increasing, impurities will result in too much chrome plating color andperformance degradation even scrapped the plating, electrolytic treatment of plating liquid and power consumption for a longtime. Ceramic diaphragm electrolytic plating solutions can effectively remove impurities in the electrolyte captions, thus improving plating quality of products, extending the life of plating.
Product specifications:
1, 400mm× 500mm × 80mm (upper mouth 390mm ~ 400mm height 485mm ~ 500mm width 80mm)
2, 160mm × 60mm × 520mm (flange 180mm× 80mm × 15mm,body 160mm × 60mm× 515mm)
3, diameter 210mm ~ 215mm, height 650mm or 560mm or 800mm
Note: 1) In order to ensure the electrolysis effect and strength of the product, the wall thickness of the product is designed to be about 5-7mm thick.
Using area of Alumina ceramic Diaphragm
Electrolytic ceramic pots is mainly used in the following two aspects in the electroplating industry.
1.Reducing Trivalent Chromium in Coarse Solution by Electrolytic Redox principle.
2.Used in decorative chromium and hard chromiumplating to remove impurities
3.Specification of Alumina Ceramic Diaphragm
| Water absorbtion | >40 |
| Grain size | 0.5-2 μm |
| Breaking strength | > 20Mpa |
| Acid fastness | >99% |
| Fastness to alkali | >94% |
| Size | 400*500*80mm,230*80*630mm |
| 160*60*530mm | |
| φ210*800mm,φ210*650mm,φ210*560mm |