Product Details:
|
| Name: | Zirconia Ceramic Rod | Bulk Density: | >6.0g/cm3 |
|---|---|---|---|
| Color: | White | Max Using Temp: | 1600℃ |
| Compressive Strength: | 3500 Mpa | Elastic Modulus: | 205 Gpa |
| High Light: | zirconia ceramic tube,zirconia ceramic rod |
||
99% Material Zirconia Ceramic Rod For Industrial Ceramic Application
Zirconia Ceramic Rod
1. Description
Zirconia/ZrO2/ Zirconium oxide is famous of its extremly density, extrodinary mechanical strength, wear and abrisive resistance, high toughtness and low thermal conductitivy and thermal expansion coefficinent. We offer a selection of different grade material for producing zirconia ceramic tube, the typical one include yittria partial stabilized, magnesia stablized zirconia.
We are capable of producing varity of zircoia ceramic rod from small size to large size.
Specification
| Shaping methods |
Dry pressing, injection, hot pressing, ISO pressing |
Precision capability | Fine grinding, CNC maching |
| Size capability | Max. OD50mm, ID1mm | Tolerance | Best to be 0.05mm |
| Color option | White, black, bule, yellow | Surface finish | Polishing, glazing |
| Visual quality: Smooth & finest surface, without any crack, porous, contamination | |||
2.Application:
It's always used as refractory ceramic parts, structure ceramic parts, ceramic wear parts, zirconia ceramic shafts, zirconia ceramic bearing.
3. Technical data
|
Item
|
Unit
|
Zirconia ceramic
|
|
Bulk density
|
g/cm3
|
6.05
|
|
Max use temperature
|
℃
|
1700
|
|
Water absorbtion
|
%
|
0
|
|
Bending Strength
|
Mpa
|
1000
|
|
Compressive Strength
|
MPa
|
3500
|
|
Thermal Expansion Coefficient
|
(x10-6/°C)
|
10
|
|
Vickers Hardness
|
HV0.5
|
1200
|
|
Linear expansion coefficient
|
x 10-6/℃
|
9
|
|
Flexural strength
|
Mpa
|
354
|
|
Elastic modulus
|
Gpa
|
205
|
|
Size
|
φ22.22*207mm
|
φ27*300mm
|