Product Details:
|
| Features: | High Temperature Resistance | Sintering Temperature: | 1700℃ |
|---|---|---|---|
| Hardness: | 1700HV | Fracture Toughness: | 3-4 |
| Density: | 3.7-3.9g/cm3 | Material: | 95% Al2O3 |
| Highlight: | porous alumina plate,alumina ceramic tube |
||
Al2o3 Plate Aluminum Oxide Ceramic High Performance Good Heat Resistance
1. Description
Alumina setter plates made of high technical ceramics belong to the category of furnace accessories. Due to their high resistance to corrosion and dimensional stability, they are primarily used by universities and research laboratories in high-temperature annealing and melting processes.
Alumina or aluminum oxide (Al2O3) in its various levels of purity is used more often than any other advanced ceramic material. Tigar Ceramic offers a wide range of material types with different property profiles that can be adjusted via a targeted matrix design.
This material has very high hardness, very high stiffness, very good corrosion resistance to chemicals at high temperature, and very high refractoriness or use temperature.
The applications for alumina advanced ceramics are heavy-duty forming tools, substrates and resistor cores in the electronics industry, tiles for wear protection and ballistics, thread guides in textile engineering, seal and regulator discs for valves, heat-sinks for lighting systems, protection tubes in thermal processes or catalyst carriers for the chemicals industry.
2.Data Sheet
| Property | Units | ||||
| Al2O3 Content | % | 96 | 98 | 99.5 | 99.7 |
| Density | g / cm3 | 3.70 | 3.80 | 3.90 | 3.92 |
| Color | - | White | White | Ivory | Ivory |
| Compressive Strength @ 25 C | Mpa | 2229 | 2091 | 2512 | 2350 |
| Tensile Strength @ 25 C | MPa | 200 | 200 | 248 | 252 |
| Flexural Strength @ 25 C | MPa | 331 | 276 | 324 | 320 |
| Elastic Modulus @ 25 C | GPa | 290 | 331 | 366 | 380 |
| Hardness : Knoop Rockwell | (Gpa) Kg/mm2 R45N |
(11.7) 1196 79 |
(12.5) 1276 77 |
(14) 1428 85 |
(15) 1510 90 |
| Thermal Conductivity @ 25 C | W / m-Deg K | 20.8 | 28.1 |
30.7 |
31.6 |
| Coefficient of Thermal Expansion @ 25-1000 C | 1 X 10-6 / Deg C |
7.9 | 8.5 | 8.1 | 8.0 |
| Specific Heat @ 25 C | cal / g / Deg C | .184 | .184 | .182 | .180 |
| Maximum Working Temp. | Deg C | 1650 | 1650 | 1700 | 1700 |
| VolumeResitivity @25C @700 C | ohm-cm ohm-cm |
1 X 10-13 1 X 10-8 |
1X 10-13 2.2 X 10-9 |
1 X 10-13 6 x 10-7 |
1 X 10-13 6 x 10-7 |
| Dielectric Strength (@Thickness) 100Mils |
ac volts per mil |
350 | 340 |
335 | 330 |
| Dielectric Constant 1Mhz @25C |
e' / eo | 8.6 | 9.4 | 9.7 | 10.0 |
| Dissipation Factor 1 Mhz @25C |
Tan Delta | .0004 |
.0003 |
.0003 |
.0002 |
3.Application