Product Details:
|
| Density: | ＞3.7g/cm3 | Name: | High Strength Textile Ceramic Eyelets For Industrial Textile Ceramic Parts |
|---|---|---|---|
| Tensile Strength @ 25 C: | ＞200 | Flexural Strength @ 25 C: | ＞276 |
| Color: | Red And White | Usage: | Industry |
| Highlight: | porous ceramic disc,alumina ceramic tube |
||
High strength Textile ceramic eyelets for industrial Textile ceramic parts
Textile Ceramic
Product Category: ceramic products
Product Features:
Ceramic porcelain eye by the precision ceramic processing, ultra-fine polishing up to Ra0.2, due to high hardness, smooth surface, enameled wire sliding in its smooth surface from damage.
Detailed Product Description:
Uses: Suitable for all kinds of winding machine and textile machinery in the wire cross-wire components. By the precision ceramic processing, ultra-fine polishing up to RA0.2.
| Property | Units | ||||
| Al2O3 Content | % | 96 | 98 | 99.5 | 99.7 |
| Density | g / cm3 | 3.70 | 3.80 | 3.90 | 3.92 |
| Color | - | White | White | Ivory | Ivory |
| Compressive Strength @ 25 C | Mpa | 2229 | 2091 | 2512 | 2350 |
| Tensile Strength @ 25 C | MPa | 200 | 200 | 248 | 252 |
| Flexural Strength @ 25 C | MPa | 331 | 276 | 324 | 320 |
| Elastic Modulus @ 25 C | GPa | 290 | 331 | 366 | 380 |
| Hardness : Knoop Rockwell | (Gpa) Kg/mm2 R45N |
(11.7) 1196 79 |
(12.5) 1276 77 |
(14) 1428 85 |
(15) 1510 90 |
| Thermal Conductivity @ 25 C | W / m-Deg K | 20.8 | 28.1 |
30.7 |
31.6 |
| Coefficient of Thermal Expansion @ 25-1000 C | 1 X 10-6 / Deg C |
7.9 | 8.5 | 8.1 | 8.0 |
| Specific Heat @ 25 C | cal / g / Deg C | .184 | .184 | .182 | .180 |
| Maximum Working Temp. | Deg C | 1650 | 1650 | 1700 | 1700 |
| VolumeResitivity @25C @700 C | ohm-cm ohm-cm |
1 X 10-13 1 X 10-8 |
1X 10-13 2.2 X 10-9 |
1 X 10-13 6 x 10-7 |
1 X 10-13 6 x 10-7 |
| Dielectric Strength (@Thickness) 100Mils |
ac volts per mil |
350 | 340 |
335 | 330 |
| Dielectric Constant 1Mhz @25C |
e' / eo | 8.6 | 9.4 | 9.7 | 10.0 |
| Dissipation Factor 1 Mhz @25C |
Tan Delta | .0004 |
.0003 |
.0003 |
.0002 |