Refractory Silicon carbide kiln shelves for industrial high temperature furnace
1. Introduction
Silicon carbide kiln shelf is combined with high purity silicon carbide and ultra fines. Shaped by vibration, made by high sintering. The SiC platesare oxide bonded silicon carbide based products, which are used in Kiln Furniture. It is featured with high bending strength at elevated temperature, good abrasion resistance, Resistance to thermal shock, high thermal conductivity and offers a good life.
Refractory high temperature silicon carbide kiln shelf is widely used to fire sanitary ceramic , daily ceramic , porcelain , and pottery.It has high strength and good quality.Commonly we coat alumina on one side, it can protect your product.In order to make sure no pollution to your products.
2. Silicon carbide kiln shelf Features
a) Excellent Thermal Shock Characteristics
b) Corrosion Resistance
c) As Cast Tight Dimensional Tolerances
d) High Creep Resistance
e) Superior Wear Resistance
f) High strength, extreme hardness,wear resistance, high temperature tolerance, corrosion resistance, oxidation resistance,thermal shock resistance, high thermal conductivity, low coefficient of thermal expansion, creep resistance under high temperature and so on.
3. Silicon carbide kiln shelf Specification
1. high mechanical strength
2. High temperature
3. High thermal conductivity.
4. 98% purity
2) Silicon carbide kiln shelf Benefits:
a) Superior Oxidation Resistance
b) Improved Performance
c) Lowered Cost Burden
d) Longer Life Between Replacement/Rebuilds
e) Allows Lower Weight
f) Very High Thermal Conductivity
4. Technical parameter
| Item | Technical Data |
| Volume density(g/cm3) | 2.70-2.75 |
| Apparent porosity(%) | 7-8 |
| Strength at normal temperature(Mpa) | >50 |
| High temperature bending strength(Mpa/1400℃) | >55 |
| Cold crushing strength(Mpa) | >90 |
| Refractoriness under load (℃) | >1750(T2)2Kg/cm2 |
| Maximum service temperature (℃) | 1450 |
| Pyroconductivity (Kcal/m.h.℃) | 13.5-14.5 |
| Thermalexpansivity(×10-6/℃) | 4.2-4.8 |
| Chemical compent | SiC>90% |
| Fe2O3<0.3% | |
| Al2O3>99%(surface coating) |