Max Temperature:1450°C
Color:Black
Chemical Resistance:Good
Application:Kiln Firing
Chemical Resistance:Good
Size:Customize
Size:Customize
Material:Silicon Carbide
Surface Type:Unglazed
Application:Kiln Firing
Durability:High
Shape:Rectangular, Square
Density:2.75g/cm3
Color:Black
Surface Type:Unglazed
Density:2.75g/cm3
Durability:High
Application:Kiln Firing
Material:Mullite and Sic
Size:310*310*12mm
Package:Wooden box
Compressive strenght >=:1300Kg/cm2
Thermal Conductivity at 1000ºC:13.5-14.5Kcal/m.hr.ºC
Thermal Expansion at 1000ºC:0.42-0.48
2kg/cm2 Load softening temperatureT2:≥1750
Cold Modulus of Rupture Mpa≥:40
Modulus of Rupture at 1400C:>550kg/cm2
Apparent porosity %≤:13-17
Cold Modulus of Rupture Mpa≥:40
(Mpa/1400℃)High temperature Bending Strength:>55
(Mpa)Room temperature flexural strength:>50
Density:>2.75g/cm3
(Mpa/1400℃)High temperature Bending Strength:>55
Open porosity:<.1%
Density:>2.75g/cm3
Modulus of elasticity:300Gpa