High Temperature Ceramic Saggers , Sintering Powder Mullite Refractory Box

Certification
China Yixing City Kam Tai Refractories Co.,ltd certifications
China Yixing City Kam Tai Refractories Co.,ltd certifications
Customer Reviews
This is the first time for our cooperation. They are indeed what we want. We look forward to working with you again in future.

—— Fred (USA)

Your ceramic tube is really good for our application, we will buy more in future.

—— Jessica Ferrara (Italy)

You are the best, your ceramic parts are perfect

—— Dalibor(Czech)

Our client satisfied with the Cordierite kiln shelf and sagger . But It would be better if the delivery time be shorter in our next order.

—— Van Nguyen (Viet Nam)

I hope you are fine and business is well. We recieved the perfect goods from you, your are the best.

—— Niko (UK)

I'm Online Chat Now

High Temperature Ceramic Saggers , Sintering Powder Mullite Refractory Box

High Temperature Ceramic Saggers , Sintering Powder Mullite Refractory Box
High Temperature Ceramic Saggers , Sintering Powder Mullite Refractory Box

Large Image :  High Temperature Ceramic Saggers , Sintering Powder Mullite Refractory Box

Product Details:
Place of Origin: CHINA
Brand Name: KAMTAI
Certification: SGS
Model Number: KTMS16
Payment & Shipping Terms:
Minimum Order Quantity: 300PCS
Price: Negotiable
Packaging Details: PLYWOOD BOX AND PALLET
Delivery Time: 25 DAYS AFTER PAYMENT
Payment Terms: L/C, T/T, Western Union, MoneyGram,Paypal
Supply Ability: 3000PCS/MONTH

High Temperature Ceramic Saggers , Sintering Powder Mullite Refractory Box

Description
Features: High Temperature Resistance Product Name: Kam Tai Refractory High Temperature Mullite Sagger For Sintering Powder
Material: Mullite Shape: Square
Density: 2.4g/cm3 MOQ: 300PCS
High Light:

ceramic saggers

,

refractory box

Kam Tai refractory high temperature mullite sagger for sintering powder

 

1. Description

A corundum mullite sagger production methods, passes through the ingredients, forming and sintering, wherein a weight percentage of ingredients: Fused mullite: 1mm <diameter d ^ 2mm pellet 10- 15% 0. 5mm <diameter d ^ Imm pellets 20-25% tabular alumina 0. 076mm <diameter d San 0. 5_ pellets 20-25% particle size <0. 076mm powder 15 22% 20-25% alumina powder microsilica 0. 5-1 0% calcium aluminate cement plus 0.5 5-1 0% 1-0 hexametaphosphate 0. 3%;... formed using gravity casting forming method; forming method is as follows: (1) the mashing: first alumina powder, silica powder, calcium aluminate cement and tabular alumina fine powder is added in dry mixing compulsory mixer; hexametaphosphate added to water to prepare six partial sodium backup solution; the mixed powder and mix well hexametaphosphate solution, to prepare a slurry; (2) mixing: in the public compound, according to first add a small pellet after pellet was added to increase the order All pellets into the small left foot forming a slurry prepared by mixing; (3) casted: molded model on the vibration table, start shaking table, the slurry was poured into a molding forming model, the edge vibration side pouring off After the mold was semi-finished products.

 

2. Technical Parameter

Deatails For Refractory kiln tray For Sintering Rare Earth Powder And Pigment

 
Mullite
DENSITY(g/cm3)
2.4
APPARENT PORSITY(%)
26.00

ROOM TEMPERATURE

FLEXURAL STRENGTH(MPA)
10.0
CYCLE USING TIMES
>60
Advantage High Strength 
Application Industrial Furnaces
Using Temperature  <1600℃
 
We can also make chage according to your using condition, a good product is not by data , it is by real performance.Seeing is believing!
 

3. Our Advantages 

WE HAVE PROFESSIONAL DETECTING EQUIPMENTWe are aimed to improve R&D and production process and equipment. Moreover, we cooperate with famous university such like Liaoning University of Science and Technology, Beijing University of Science and Technology.

 

 
 

Contact Details
Yixing City Kam Tai Refractories Co.,ltd

Contact Person: tao

Send your inquiry directly to us (0 / 3000)

Leave a Message

We will call you back soon!