Product Details:
|
| Name: | Factory Price High Temperature Resistance Alumina Ceramic Kiln Stilts | Material: | 95% Alumina Ceramic |
|---|---|---|---|
| Shape: | Triangle | Type: | Kiln Stilts |
| Application: | Refractory, Industrial Ceramic | Package: | Carton Box |
| High Light: | porous alumina plate,alumina ceramic tube |
||
Factory Price High Temperature Resistance Alumina Ceramic kiln stilts
1. Description
Aluminum oxide (Al2O3), commonly known as alumina, is extensively used as an engineering ceramic due to its high performance at a cost-effective price. Typically, alumina is available in grades from 88% to 99.99% purity with properties varying accordingly. Zirconia-toughened alumina is a modified, stronger grade of alumina.
Alumina components can be manufactured by a number of different methods including pressing, extruding, slip casting and injection molding. The method of manufacture generally depends on the size and quantity of components required.
Alumina ceramic starts the manufacturing process as a powder which, once compressed, can be machined if required (known as “green machining”) before being fired. After firing, further processing can only be carried out using diamond tooling.
It could be argued that alumina is one of the most cost-effective of all ceramic materials, and as a result is one of the most widely used. Its combination of high thermal conductivity and low thermal expansion imparts good thermal shock resistance.
| Property | Units | ||||
| Al2O3 Content | % | 96 | 98 | 99.5 | 99.7 |
| Density | g / cm3 | 3.70 | 3.80 | 3.90 | 3.92 |
| Color | - | White | White | Ivory | Ivory |
| Compressive Strength @ 25 C | Mpa | 2229 | 2091 | 2512 | 2350 |
| Tensile Strength @ 25 C | MPa | 200 | 200 | 248 | 252 |
| Flexural Strength @ 25 C | MPa | 331 | 276 | 324 | 320 |
| Elastic Modulus @ 25 C | GPa | 290 | 331 | 366 | 380 |
| Hardness : Knoop Rockwell | (Gpa) Kg/mm2 R45N |
(11.7) 1196 79 |
(12.5) 1276 77 |
(14) 1428 85 |
(15) 1510 90 |
| Thermal Conductivity @ 25 C | W / m-Deg K | 20.8 | 28.1 |
30.7 |
31.6 |
| Coefficient of Thermal Expansion @ 25-1000 C | 1 X 10-6 / Deg C |
7.9 | 8.5 | 8.1 | 8.0 |
| Specific Heat @ 25 C | cal / g / Deg C | .184 | .184 | .182 | .180 |
| Maximum Working Temp. | Deg C | 1650 | 1650 | 1700 | 1700 |
| VolumeResitivity @25C @700 C | ohm-cm ohm-cm |
1 X 10-13 1 X 10-8 |
1X 10-13 2.2 X 10-9 |
1 X 10-13 6 x 10-7 |
1 X 10-13 6 x 10-7 |
| Dielectric Strength (@Thickness) 100Mils |
ac volts per mil |
350 | 340 |
335 | 330 |
| Dielectric Constant 1Mhz @25C |
e' / eo | 8.6 | 9.4 | 9.7 | 10.0 |
| Dissipation Factor 1 Mhz @25C |
Tan Delta | .0004 |
.0003 |
.0003 |
.0002 |
3. Application
Electric appliance industry/Automotive industry/Mechanical industry
Engineering industry/Electrical heating element industry/LED Lighting Industry
We have professional equipment and we are very professional manufacturer.
When we produce alumina ceramic, we use the best raw material of high pure alumina powder.
And we use dry press and injection moulding,cast moulding to mould alumina ceramic substrate.
We can customize according to your requirement.