Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm

Certification
China Yixing City Kam Tai Refractories Co.,ltd certification
China Yixing City Kam Tai Refractories Co.,ltd certification
Customer Reviews
This is the first time for our cooperation. They are indeed what we want. We look forward to working with you again in future.

—— Fred (USA)

Your ceramic tube is really good for our application, we will buy more in future.

—— Jessica Ferrara (Italy)

You are the best, your ceramic parts are perfect

—— Dalibor(Czech)

Our client satisfied with the Cordierite kiln shelf and sagger . But It would be better if the delivery time be shorter in our next order.

—— Van Nguyen (Viet Nam)

I hope you are fine and business is well. We recieved the perfect goods from you, your are the best.

—— Niko (UK)

I'm Online Chat Now

Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm

Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm
Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm

Large Image :  Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm

Product Details:
Place of Origin: CHINA
Brand Name: KAMTAI
Certification: ISO
Model Number: KTRKF7
Payment & Shipping Terms:
Minimum Order Quantity: 3000 PCS
Price: Negotiable
Packaging Details: PLYWOOD BOX AND PALLET
Delivery Time: 25 DAYS AFTER PAYMENT
Payment Terms: T/T, L/C, Western Union, MoneyGram,Paypal
Supply Ability: 50000PCS/MONTH

Lightweight Insulating Fire Brick , White Mullite Insulating Brick 230 * 114 * 65mm

Description
Color: White Using Temperature: 1300-1600℃
Density: 0.6-1.2g/cm3 Al2O3 ≥%: 40
Fe2O3 ≥%: 0.7 Size: 230*114*65/75mm
High Light:

alumina ceramic disc

,

high alumina kiln shelves

High heat refractory kiln furniture Mullite lightweight insulation brick 230 * 114 * 65mm

 

1. Description 

Mullite (3 2 sio2, al2o3) phase of high aluminum refractory material. General alumina content is between 65% ~ 75%. Mineral composition in addition to the mullite, contain the alumina lower also contains a small amount of glass phase and cristobalite; Containing alumina high contains a small amount of corundum.High refractoriness, can reach more than 1790 ℃. The rul start temperature of 1600 ~ 1700 ℃. Room temperature compressive strength of 70 ~ 260 mpa. Good thermal shock resistance. A sintered mullite bricks and two fused mullite brick.

Sintered mullite brick with high bauxite clinker as the main raw material, add a small amount of clay or raw bauxite as binder, forming, sintering and made. Fused mullite brick with high alumina, alumina industry and refractory clay as raw material, adding charcoal or coke fine as a reducing agent, reduction fused method is used to manufacture after forming.

 

2. Specification

Item 1300 1450 1550 1650 0.5
ASTM C155-84 Classification 23 26 28 30  
ISO 2245 Classification 125-0.5-L 140-0.8-L 150-0.9-L 160-1.0-L  
Classification Temperature 1260 1430 1540 1650  

g/cm³

Bulk Density

ASTM C-134-84

0.6 0.8 0.9 1.0 0.55

Cold Crushing Strength

ASTM C-93-847(MPa)

 

1.5 3.0 3.5 4.0 1.2
Thermal Expansion At 1100℃ 0.5 0.5 0.58 0.6 ≤1.5(900℃)
Thermal shock Resistance Cycles 30 30 30 30  
Thermal Conductivity ASTM C182-88W/m.k 400 0.14 0.27 0.32 0.41 ≤0.15
600 0.16 0.29 0.34 0.43  
800 0.18 0.31 0.36 0.44  
1000 0.20 0.33 0.38 0.45  
1200 0.35 0.41 0.47  
Al2O3 % 37 52 67 73  
Fe2O3 % 1.3 1.0 0.8 0.6  
 

3. Features

Low Thermal Conductivity

It has good insulation effect and can thin the thickness of furnace wall.

Low thermal capacity

Less heat storage, it has good usage effect in intermittent furnace.

Good thermal shock resistance and high temperature strength

It can prolong the service life of kilns and prevent dirty slag to drop down.

Precise dimension

It can keep uniform gaps between each brick, speed up the building, guarantee the integrated high strength of the masonry.

Low impurity

Lower iron and alkali content, it has high resistance to reduce atmosphere corrosion at high temperature.

 

4. Application 

It is mainly used for hot blast stove top, blast furnace and furnace bottom, the regenerator of glass furnace, ceramic sintering kiln, petroleum cracking system corner lining, etc. Also widely used in hot blast stove, metal furnace, ceramic tunnel kilnelectrical porcelain shuttle kiln, etc., has a broad market prospect.

 

 

 

 

 

 